ALL PRODUCT
![]()
Flux & Wire Combination
S-300B x YS-308L, YS-309L, YS-316L, YS-347
Superflux 300S S-300B x YS-308L, YS-309L, YS-316L, YS-347
| Type | |
|---|---|
| Industry |
| JIS | Z3352 SA AF2 |
|---|---|
| EN | ISO 14174-S A AF 2 |
| KS | |
| AWS |
- Caution .
- Purpose .
- Attribute .
Superflux300S x YS-316(L)
-
Caution
① Dry the flux at 300~350°C (572~662°F ) for 60 minutes before use.
② Avoid using high current to prevent harming of corrosion-resistibility in heat-affected zone, heat input in welding should be kept as low as possible.
③ Welding in groove should be done in 2 passes to ease slag removal. - Purpose ① 18%Cr-8%Ni stainless steel
-
Attribute
① Good resistance to crack and corrosion
② Easy to remove slag
③ Good bead appearance
④ Density : 1.2g/cm3
Superflux300S x YS-309(L)
-
Caution
① Dry the flux at 300~350°C (572~662°F ) for 60 minutes before use.
② Avoid using high current to prevent harming of corrosion-resistibility in heat-affected zone, heat input in welding should be kept as low as possible.
③ Welding in groove should be done in 2 passes to ease slag removal." - Purpose ① 18%Cr-8%Ni stainless steel
-
Attribute
① Good resistance to crack and corrosion
② Easy to remove slag
③ Good bead appearance
④ Density : 1.2g/cm3
Superflux300S x YS-308(L)
-
Caution
① Dry the flux at 300~350°C (572~662°F ) for 60 minutes before use.
② Avoid using high current to prevent harming of corrosion-resistibility in heat-affected zone, heat input in welding should be kept as low as possible.
③ Welding in groove should be done in 2 passes to ease slag removal. - Purpose ① 18%Cr-8%Ni stainless steel
-
Attribute
① Good resistance to crack and corrosion
② Easy to remove slag
③ Good bead appearance
④ Density : 1.2g/cm3